HP2023JN is a Low Density Polyethylene grade suitable for general-purpose packaging. They exhibit better draw down, good optical and mechanical properties. HP2023JN contains slip and antiblock additives.
DESCRIPTION
HP2023JN is a Low Density Polyethylene grade suitable for general-purpose packaging. They exhibit better draw down, good optical and mechanical properties. HP2023JN contains slip and antiblock additives. TYPICAL
APPLICATIONS
Thin shrink film, lamination film, produce bags, textile packaging, soft goods packaging, general-purpose bags with good optics and t-shirts carrier bags.
PROCESSING CONDITIONS
Typical processing conditions for HP2023JN are:
Barrel temperature: 160 - 190°C
Blow up ratio: 2.0 - 3.0
| SABIC HP2023JN | |||
| Low Density Polyethylene | |||
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
| POLYMER PROPERTIES | |||
| Melt Flow Index | 2.0 | g/10 min | ASTM D-1238 |
| Density @ 23 °C | 923 | g/m3 | ASTM D-1505 |
| FILM PROPERTIES | |||
| Tensile Properties | |||
| stress at break, MD | 20 | MPa | ASTM D882 |
| stress at break, TD | 15 | MPa | ASTM D882 |
| stress at break, TD | 300 | % | ASTM D882 |
| stress at break, MD | 588 | % | ASTM D882 |
| stress at yield, MD | 12 | MPa | ASTM D882 |
| stress at yield, TD | 12 | MPa | ASTM D882 |
| 1% secant modulus, MD | 235 | MPa | ASTM D882 |
| 1% secant modulus, TD | 271 | MPa | ASTM D882 |
| Tear Resistance | |||
| MD | 15 | g/µm | ASTM D1922 |
| TD | 11 | g/µm | ASTM D1922 |
| THERMAL PROPERTIES | |||
| Vicat Softening Temperature | 92 | °C | ASTM D1525 |
DESCRIPTION
HP2023JN is a Low Density Polyethylene grade suitable for general-purpose packaging. They exhibit better draw down, good optical and mechanical properties. HP2023JN contains slip and antiblock additives. TYPICAL
APPLICATIONS
Thin shrink film, lamination film, produce bags, textile packaging, soft goods packaging, general-purpose bags with good optics and t-shirts carrier bags.
PROCESSING CONDITIONS
Typical processing conditions for HP2023JN are:
Barrel temperature: 160 - 190°C
Blow up ratio: 2.0 - 3.0