HS code:
3902100090
Melt flow rate:
25 g/10min
Grade:
Injection molding grade
Packing:
25 kg/bag
Brand:
SINOPEC
Moplen HP561R is a polypropylene homopolymer used for extrusion applications. Moplen HP561R has a very narrow molecular weight distribution and is formulated with an anti-gasfading stabilisation package. Moplen HP561R is used for the production of continuous filaments. Typical applications are high-tenacity yarns (HTY) and spunbond nonwovens.
This grade is not intended for medical and pharmaceutical applications. Status Commercial: Active Availability Africa-Middle East; Asia-Pacific; Europe Application Absorption & Filtration; Filament Yarn; Furniture & Buildings; Geotextile & Agriculture; Hygiene Nonwoven; Nonwovens; Wipes/Tissues Market Textile Processing Method Continuous Filament/Spinning; Extrusion Coating; Fibers; Spunbond Attribute Controlled Rheology; Gas-fading Resistant; High Flow; Homopolymer; Narrow Molecular Weight Distribution.
The resin is packed in 25 kg bags, octabins or bulk containers protecting it from contamination. If it is stored under certain conditions, i. e. if there are large fluctuations in ambient temperature and the atmospheric humidity is high, moisture may condense inside the packaging. Under these circumstances, it is recommended to dry the resin before use. Unfavorable storage conditions may also intensify the resin's slight characteristic odor. Resin should be protected from direct sunlight, temperatures above 40°C and high atmospheric humidity during storage. Higher storage temperatures may reduce the storage time. The information submitted is based on our current knowledge and experience. In view of the many factors that may affect processing and application, these data do not relieve processors of the responsibility of carrying out their own tests and experiments; neither do they imply any legally binding assurance of certain properties or of suitability for a specific purpose. This information does not remove the obligation of the customer to inspect the material on arrival and notify us of any faults immediately. It is the responsibility of those to whom we supply our products to ensure that any proprietary rights and existing laws and legislation are observed
Typical Properties | Nominal Value |
Units |
Test Method |
Physical | |||
Melt Flow Rate, (230 °C/2.16 kg) | 25 | g/10 min | ISO 1133-1 |
Density | 0.900 | g/cm³ | ISO 1183-1 |
Mechanical | |||
Flexural Modulus | 1150 | N/mm² | ISO 178 |
Tensile Stress at Break, (23 °C, 50 mm/min) | 20 | N/mm² | ISO 527-1, -2 |
Tensile Stress at Yield, (23 °C, 50 mm/min) | 33 | N/mm² | ISO 527-1, -2 |
Tensile Strain at Break, (23 °C, 50 mm/min) | 650 | % | ISO 527-1, -2 |
Tensile Strain at Yield, (23 °C, 50 mm/min) | 11 | % | ISO 527-1, -2 |
Thermal | |||
Vicat Softening Temperature, (A50) | 151 | °C | ISO 306 |
Deflection Temperature Under Load, (0.45 MPa, 74 | °C | ISO 75B-1, -2 | |
Ask a quote for the latest price and one of our team members will respond as soon as possible. Fields marked with * are required.